polyester film and rubber adh. polyester film and silicone adh. polyester film and acrylic adh. PET Film glass fibres reinforced Packaging & sizes |
|
| Type | Colour | Backing | Backing thickness (µm) |
Total thickness (µm) |
Adhesive Type | Peel adhesion (N/cm) |
Tensile strength (N/cm) |
Elongation % | Breakdown voltage kV |
Thermal Class (°C) |
Short Time (°C) |
|---|---|---|---|---|---|---|---|---|---|---|---|
P.31 ![]() | ![]() ![]() ![]() ![]() |
PET | 23 | 60 | R-TX | 5.00 | 40 | 90 | 4,5 | 130 | |
| Good adhesion and comformability. Very thin Film (1 mil). For coils outer and interlayer insulation. | |||||||||||
11 B* ![]() | ![]() |
PET | 23 | 60 | R-TX | 4.05 | 35 | 80 | 4,5 | 130 | |
| Thin film tape: multi purpose coil and small transformers insulation. | |||||||||||
| P.231 | ![]() |
PET | 23 | 100 | R-TX | 6.00 | 40 | 90 | 4,5 | 130 | |
| Double sided adhesive for components bonding. | |||||||||||
| 211 B* | ![]() |
PET | 23 | 90 | R-TX | 5.00 | 35 | 80 | 4,5 | 130 | |
| Double coated tape for assembling and bonding electrical components. | |||||||||||
P.315 ![]() | ![]() ![]() |
PET | 50 | 90 | R-TX | 5.00 | 70 | 90 | 9 | 130 | |
| Higher thickness and tessile strengh. For small transformers and coils insulation. | |||||||||||
12 B* ![]() | ![]() |
PET | 50 | 90 | R-TX | 4.05 | 65 | 80 | 8,5 | 130 | |
| Thicker film for heavy duty coils and transformers. | |||||||||||
Reserved Area
Search
| legenda | ||
|---|---|---|
| * | ![]() |
|
| * | Tempo di stoccaggio 6 mesi | |
| ® | DuPont De Nemours reg. Trade Mark | |
| ® | Kemica spa reg. Trade Mark | |
| ® | Ultern GE Plastic reg. Trade Mark | |
![]() |
Underwriters Laboratories Inc.File n. E 178430 | |
![]() |
Clear | |
![]() |
Translucent | |
| PTFE | Polytetrafluorethylene | |
| PE | Polyethylene | |
| PET | Polyester (Polyethylene terephtalate) |
|
| PET-HT | PET Heat Stabilized | |
| PEN | Polyethylene naftenate | |
| PEI | Polyetherimide | |
| ACR | Acrylic | |
| SIL | Silicone | |
| R-TX | Crosslinked rubber | |
| R-TS | Thermosetting rubber | |